Liqui Moly LM 203 Mos2 Anti-Friction Lacquer 1KG - 4033

Rapid drying, resin-bound MoS2 anti-friction lacquer dispersed in solvent. Produces a solid adherent film of dry lubricant with low friction values.

Used as a pre-treatment for drive elements under heavy loading such as gearwheels, racks, profiled shafts, and joints. Lubrication during the assembly of press fittings, treatment of work pieces and tools for metal forming and metal processing.

APPLICATION

• Surfaces to be coated must be bare metal, free from grease and dry
• Lightly roughening the surface by sand blasting, grinding with emery, pickling or phosphating will produce the optimum service life for the film
• Application with paint spray gun (0.8 mm nozzle/2-3 bar) or application by immersion or brush also possible (recommended coating thickness 5-15 µm)
• The product can also be diluted with acetone, ethyl acetate, methyl ethyl ketone, methyl isobutyl ketone, ethyl glycol acetate and isopropyl alcohol
• The drying time depends on the evaporation number of the solvent used
• The solvents used with the original product guarantee that the lubricating film will be dry after just 10 minutes
• Maximum hardness, adhesive strength and wear life after 1-2 hours
• The drying process can be accelerated by exposing to high temperatures